A simple, low-cost, and nontoxic aqueous ink chemistry is described for digital printing of ZnO films. Selective design through controlled precipitation, purification, and dissolution affords an aqueous Zn(OH)(x)(NH3)y((2) (x)+) solution that is stable in storage, yet promptly decomposes at temperatures below 150 degrees C to form wurtzite ZnO. Dense, high-quality, polycrystalline ZnO films are deposited by ink-jet printing and spin-coating, and film structure is elucidated via X-ray diffraction and electron microscopy. Semiconductor film functionality and quality are examined through integration in bottom-gate thin-film transistors. Enhancement-mode TFTs with ink-jet printed ZnO channels annealed at 300 degrees C are found to exhibit strong field effect and excellent current saturation in tandem with incremental mobilities from 4-6 cm(2) V-1 s(-1). Spin-coated ZnO semiconductors processed at 150 degrees C are integrated with solution-deposited aluminum oxide phosphate dielectrics in functional transistors, demonstrating both high performance, i.e., mobilities Up to 1.8 cm(2) V (1) s (1), and the potential for low-temperature solution processing of all-oxide electronics.