A pressing problem in supported-metal-nanoparticle heterogeneous catalysis-despite the long history and considerable fundamental as well as industrial importance of such heterogeneous catalysts-is how to monitor such catalysts' formation more routinely, rapidly, and in real time. Such information is needed to better control the size, shape, composition, and thus resultant catalytic activity, selectivity, and lifetime of these important catalysts. To this end, a study is reported of the formation of supported Pt(0)(n), nanoparticles by H-2 reduction of H2PtCl6 on Al2O3 (or TiO2) to give 6 equivalents of HCl plus supported Pt(0)(n)/Al2O3 (or Pt(0)(n)/TiO2), all while in contact with a solution of EtOH and cyclohexene. The HCl and Pt(0)(n) products were confirmed, respectively, by the stoichiometry of HCI formation using pH(apparent) measurements, appropriate standards, and by TEM and EDX measurements. The hypothesis of this research is that the kinetics of formation of this supported heterogeneous catalyst could be successfully monitored by a fast cyclohexene hydrogenation catalytic reporter reaction method first worked out for monitoring transition-metal nanoparticle formation in solution (Watzky, M. A.; Finke, R. G. J. Am. Chem. Soc. 1997, 119, 10382-10400). Significantly, sigmoidal kinetics of Pt(0)(n)/Al2O3 catalyst formation were in fact successfully monitored by the catalytic hydrogenation reporter reaction method and then found to be well fit to the Finke-Watzky (hereafter F-W) 2-step, slow continuous nucleation and then autocatalytic surface growth mechanism, A -> B (rate constant k(1)) and A + B -> 26 (rate constant k(2)), respectively, in which A is the H2PtCl6 and B is the growing, catalytically active Pt(0) nanoparticle surface. The finding that the F-W mechanism is applicable is significant in that it, in turn, suggests that the >= 8 insights from studies of the mechanisms of soluble nanocluster formation can likely also be applied to supported heterogeneous catalyst synthesis, including a recent equation that gives nanocluster size vs time in terms of k(1), k(2), [A](0), and other parameters (Watzky, M. A.; Finney, E. E.; Finke, R. G. J. Am. Chem. Soc. 2008, 130,11959-11969). Also presented are the use of the catalytic reporter reaction to reveal H-2 gas to-solution mass-transfer-limitations (MTL) in the system of H2PtCl6 on TiO2, results relevant to a recent communication in this journal. The use of the F-W 2-step nucleation and autocatalytic growth kinetic model to fit 3 literature examples of heterogeneous catalyst formation, involving H-2 reduction of both supported or bulk MxOy (i.e., and in gas-solid reactions), are also presented as part of the Supporting Information. A conclusion section is then provided summarizing the insights and caveats from the present work, as well as some needed future studies.