Plasma Enhanced Chemical Vapor Deposition (PECVD) of poly-2-hydroxyethyl methacrylate (pHEMA) biocompatible, biodegradable polymer films were produced alone and cross-linked with ethylene glycol diacrylate (EGDA). Degree of cross-linking was controlled via manipulation of the EGDA flow rate, which influenced the amount of swelling and the extent of degradation of the films in an aqueous solution over time. Noncross-linked pHEMA films swelled 10% more than cross-linked films after 24 h of incubation in an aqueous environment. Increasing degree of film cross-linking decreased degradation over time. Thus, PECVD pHEMA films with variable cross-linking properties enable tuning of gel formation and degradation properties, making these films useful in a variety of biologically significant applications.