Iron- and europium-doped (<= 1 at.%)TiO2 nanoparticles powders have been synthesized by a hydrothermal route at 200 degrees C, starting with TiCl4, FeCl3 center dot 6H(2)O and EuCl3 center dot 6H(2)O. The structure, morphology and optical peculiarities were investigated by means of X-ray diffraction (XRD), transmission electron microscopy (TEM), extended X-ray absorption fine structure (EXAFS), Mossbauer spectroscopy and UV-vis measurements. The photocatalytic performance was analysed in the photodegradation reaction of phenol. Rietveld refinements of XRD patterns reveal that the as-prepared samples consist in iron- and europium-doped TiO2 in the tetragonal anatase structural shape, with particle size as low as 15 nm. By means of Mossbauer spectroscopy on both Fe-57 and Eu-151 isotopes as well as by EXAFS analyses, the presence of Fe3+ and/or Eu3+ ions in the nanosized powders has been evidenced. It was found that iron and europium ions can substitute for titanium in the anatase structure. From the UV-vis reflection spectra, by using the transformed Kubelka-Munk functions, the band gap energy (E-g) of the hydrothermal samples has been determined in comparison with that of Degussa P-25 photocatalyst. A decrease of E-g from 2.9eV found for Degussa photocatalyst to 2.8 eV for the titania doped with 1 at.% Fe has been evidenced, indicating a valuable absorption shift (similar to 20 nm) towards visible light region. However, the best photocatalytic activity in the photodegradation reaction of phenol was evidenced for the hydrothermal sample, TiO2: 1 at.% Fe, 0.5 at.% Eu, in both UV and visible light regions. The photocatalytic activities of iron-doped and iron-europium-codoped samples are high and practically the same only in visible light. The photocatalytic properties in Correlation with the structural and optical peculiarities of the hydrothermal samples are discussed. (C) 2008 Elsevier B.V. All rights reserved.