Good transparent bulk single crystals of L-alanine (nonlinear optical material) have been grown successfully by slow cooling technique from aqueous solution at pH value of 2.0. Optically transparent crystals with dimensions 2.4cm x 1.2 cm x 1.6 cm, were grown by optimizing the growth parameters within a growth period of 2 weeks. The crystallinity Of L-alanine crystal was confirmed by the powder X-ray diffraction study and diffraction peaks are indexed. The vibrational structure of the molecule is elucidated from FTIR spectra. The thermal behaviour of the grown crystal was investigated by thermogravimetric (TG) and differential thermal analyses (DTA) techniques in a nitrogen atmosphere. The result showed that the material starts decomposing at 297 degrees C. Its optical behaviour has been examined by UV-vis spectral analysis, which shows the absence of absorbance between the wavelengths ranging from 200 to 1200 nm. The NLO property was confirmed by the powder technique of Kurtz and Perry. The dielectric behaviour of the sample was also studied for the first time. (C) 2008 Elsevier B.V. All rights reserved.