Polypyrrole has been chemically synthesized on thin film nanostructures obtained from comb-shaped supramolecules of polystyrene-block-poly(4-vinyl pyridine) (PS-b-P4VP) hydrogen bonded with pentadecylphenol (PDP). PDP was washed from thin films of cylindrical and lamellar self-assembled combcopolymer systems, which resulted in removal of the upper layers of microdomains, leaving single cylindrical and lamellar layers covering a substrate, with P4VP segregated at the bottom as well as at the free air interface. This P4VP was complexed with Cu2+ ions, after which chemical oxidation polymerization of pyrrole resulted in a thin polypyrrole layer covering the nanostructured block copolymer. The use of a catalytic amount of bipyrrole greatly improved the quality of the obtained product. The conductivity was measured to be similar to 0.7 S cm(-1). (C) 2009 Elsevier Ltd. All rights reserved.