This paper focuses on the characterization of carbide lime (CL) - a by-product of acetylene production, composed mainly of calcium hydroxide with minor parts of carbonate - and compares its features to those of "dry" hydrated lime (HL) commonly used as a building material. Chemical, thermogravimetric and X-ray diffraction analyses indicated that the limes are similar in chemical and mineralogical compositions. except for the presence of carbon in the waste. Morphological and elemental chemical analyses by SEM and EDS revealed that CL particles differ from HL ones in their morphology and by the presence of carbon formations, Physical characterization included density and BET surface area of the materials. as well as, their particle size distributions in deionized water at diverse time periods. CL underwent agglomeration after approximately 60 min in water, whereas HL progressively became finer with time as determined by laser diffraction. In addition, water retention and squeeze flow tests were used to assess the pastes' fresh properties. (c) 2009 Elsevier B.V. All rights reserved.