Effect of polyacrylic acid (PAA) binder system on the development of particle orientation during uniaxial pressing is reported. Granules of different properties were compacted using uniaxial pressing at various pressure and their degree of particle orientation (DPO) was determined. The increment trend of DPO varies with granule strength and shows higher value for binder system of higher flexibility. Anisotropic shrinkage related to particle orientation is shown by compact of higher relative density (RD) and DPO; whereas anisotropic shrinkage related to non-uniform packing density is shown by compact of lower RD and DPO. Anisotropic shrinkage remains in the former compact while isotropic shrinkage was obtained for the latter compact at sintering temperature of 1600 degrees C. Subsequent cold isostatic pressing increases DPO and sintering shrinkage ratio of uniaxially pressed compacts. (c) 2009 Elsevier B.V. All rights reserved.