A simple chemical method has been developed for preparation of Ag nanoparticles dispersed on mesoporous silicate matrix, SBA-15. Ag nanoparticles were uniformly dispersed on SBA-15 matrix by using the reduction reaction of AgNO3 with trisodium citrate. The synthesized materials were characterized by using room temperature powder XRD analysis, N-2 adsorption-desorption isotherm, high resolution TEM and SEM. It was observed that the synthesized SBA-15 and Ag-SBA-15 have a surface area of 778 and 151 m(2)/g respectively. The synthesized materials have long range ordering of pores with narrow pore size distribution centered at similar to 7 nm. Pore structure of SBA-15 remains preserved even after deposition of Ag nanoparticle. This chemical route reported here offers a simple method for preparation of Ag-SBA-15, where unagglomerated Ag nanoparticles (similar to 20 nm) are uniformly dispersed on SBA-15. (C) 2010 Elsevier B.V. All rights reserved.