Solid State Ionics, Vol.181, No.1-2, 53-58, 2010
The oxygen permeation characteristics of Bi-1 (-) xSrxFeO3 mixed ionic and electronic conducting ceramics
The perovskite oxides in the system Bi-1 (-) xSrxFeO3-delta (x = 0.05, 0.15, 0.3. 0.6, and 0.8) were characterized in the intermediate temperature range (650 to 800 degrees C) by oxygen permeation and electrical conductivity measurements. The samples exhibited a single phase perovskite structure with a decreasing lattice constant with increasing Sr concentration and a structural change from rhombohedral to cubic at x >= 0.3. Mixed conductivity was confirmed in all samples with maximum flux levels on the order of 0.11 mu mol/cm(2) s at 800 degrees C for the x = 0.8 composition. Materials studied displayed p-type conductivity over the oxygen partial pressure range present in permeation measurements (0.21 to 10(-6) atm). A local maximum of oxygen flux and ionic conductivity was found near x = 0.3. (C) 2009 Elsevier B.V. All rights reserved.