Uranium dioxide films were deposited on Si (1 1 1) substrates by dc magnetron sputtering method at different sputtering parameters. The structure, morphology and chemical state of the films were studied by field emission scanning electronmicroscopy, X-ray diffraction, X-ray photoelectron spectroscopy and atomic force microscopy. Influences of film thickness on the microstructure and optical properties were investigated. Experimental results show that the film crystallites are preferentially oriented with the (1 1 1) planes. The average grain size increases with increasing film thickness. AFM images show that the root mean square roughness of the films is between 1.2 nm and 2.1 nm. Optical constants (refractive index, extinction coefficient) of the films in the wavelength range of 350-1000 nm are obtained by ellipsometric spectroscopy. The result shows that the refractive index decreases with the increasing film thickness, while extinction coefficient increases with the film thickness. (C) 2009 Elsevier B.V. All rights reserved.