Nanostructured titanium dioxide (TiO2) thin films have been prepared on metal substrates using a facile layer-by-layer dip-coating method. The phase structure and morphologies of preparing samples were characterized by means of X-ray powder diffraction (XRD) and field-emission scanning electron microscopy (FESEM). The results confirm that films are highly crystalline anatase TiO2 and free from other phases of titanium dioxide. Scanning electron microscopy (SEM) shows that the nanoparticles are sintered together to form a compact structure. The electrical properties of samples were investigated by cutternt-voltage analysis, the result indicates that a rectifying junction between the nanocrystalline TiO2 film and metal substrate was formed. The photoelectrochemical characteristics recorded under 1.5 AM illumination indicates that the as-fabricated thin film electrode possesses the highest photocurrent density at 450 degrees C, which is 1.75 mA/cm(2) at 0 V vs. Ag/AgCl. (C) 2009 Elsevier B. V. All rights reserved.