The relations between chemical structures of BM-DVB copolymers obtained with various monomer molar ratios and their carbonization products were studied. Three porous copolymers 1: 4, 1: 1, and 4: 1 of BM to DVB were the starting materials for preparation of active carbons. Two activation agents were employed: air and phosphoric acid. The carbonization process was performed in the same way in these two cases. To characterize the obtained materials FTIR spectroscopy, thermal and elemental analyses were applied. Porous structure parameters were obtained by means of nitrogen sorption. The results proved that differences in the molar ratio of monomers used in the syntheses of polymeric precursor play a key role for structure and properties of copolymers but have rather small influence on properties of the obtained carbons. Preliminary treatment is more effective during the activation process. The carbons obtained by activation with phosphoric acid are microporous and have well developed porous structures. The air activated carbons are mesoporous with specific surface areas similar to those of polymeric precursors. (C) 2010 Elsevier B.V. All rights reserved.