Anodized composite films containing superfine Al2O3 and PTFE particles were prepared on 2024 Al alloy using an anodizing method. The microstructures and properties of the films were studied by scanning electron microscopy, optical microscopy and X-ray diffraction. Friction wear tests were performed to evaluate the mechanical properties of the composites. Results indicate that the composite films with reinforced Al2O3 and PTFE two-particles have reduced friction coefficients and relatively high microhardness. The friction coefficient can be as small as 0.15, which is much smaller than that of an oxide film prepared under the same conditions but without adding any particles (0.25), while the microhardness can reach as high as 404 HV. When rubbed at room temperature for 20 min during dry sliding friction tests, the wear loss of the film was about 16 mg, which is about the half of that of the samples without added particles. The synthesized composite films that have good anti-wear and self-lubricating properties are desirable for oil-free industrial machinery applications. (C) 2010 Elsevier B.V. All rights reserved.