An atmospheric surface modification using plasma treatment method was applied to butadiene rubber to improve its adhesion strength by plate type reactor. In order to investigate the optimum reaction condition of plasma treatment, type of reaction gas(nitrogen, argon, oxygen, air), gas flow rate(30~100 mL/min), treated time(0~30 s) and primer modification method(GMA, 2-HEMA) were examined in a plate type plasma reactor. The results of the surface modification with respect to the treatment procedure was characterized by using SEM and ATR-FTIR. As the gas flow rate and treated time increases the contact angle decreases. The greatest adhesion strength was achieved at optimum condition such as flow rate of 60 mL/min, treated time 5 s and modification primer containing 2-HEMA for air. Due to the atmospheric surface modification using plate plasma method consequently reduced the wettability of butadiene rubber and resulted in the improvement of the adhesion.