Depassivation-repassivation behavior on a pure iron surface in borate buffer solution was examined under potentiostatic control by a micro-indentation test. Current peaks emerge during both downward and upward drives of the indenter due to depassivation which is caused by plastic deformation of the substrate but not elastic deformation and repassivation. The total electric charge of the current peaks is proportional to the maximum load. The total electric charge also increases with increase in intermission time of the indentation, indicating that the passive film is ruptured even during stress relaxation. It is estimated from the electric charge balance that 82% and 18% of the film rupture occurs during the downward drive and intermission, respectively, and that no rupture occurs during the upward drive. Furthermore, the film-ruptured area is estimated to be 80% of the plastic deformed surface area. The partial retainment of the passive film on iron suggests that the ductility of the passive film is higher than that of the substrate. (c) 2009 Elsevier Ltd. All rights reserved.