Novel polymer electrolyte membranes containing the sulfonic acid groups attached on polymer backbone and side group simultaneously were synthesized. The bromo-poly(2,6-dimethyl-1,4-phenylene oxide)-co-(2,6-diphenyl-1,4-phenylene oxide) copolymer (BrcoPPO) was prepared by oxidative coupling polymerization with 2,6-dimethyl phenol, 2,6-diphenyl phenol, CuCl(I) and pyridine, and followed by bromination with bromine. Copolymer was maintained in 2,6-diphenyl phenol 10 mol% and 2,6-dimethyl phenol 90 mol%. Sulfonation of BrcoPPO (S-BrcoPPC) was carried out in a chlorobenzene solvent using chlorosulfonic acid. The polymeric membranes were cast from dimethylsulfoxide solution. The membranes were studied by nuclear magnetic resonance (NMR), differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA). Sorption experiments were conducted to observe the interaction of sulfonated polymers with water and methanol. S-BrcoPPO membranes exhibited proton conductivities from 2.3 x 10(-3) to 1.4 x 10(-2) S/cm, water uptake from 7.00 to 49.43%, IEC from 0.58 to 1.38 mequiv./g, methanol permeability from 1.9 x 10(-7) to 3.5 x 10(-7) cm(2)/S (C) 2009 Published by Elsevier Ltd.