Novel hierarchical rose bridal bouquet- and humming-top-like nanostructured TiO2 were successfully prepared by the simple process with the hydrothermal temperature as the morphology-controlling factor. The gradual transformation from layered titanate to brookite phase was well consistent with the formation mechanism of the hierarchical morphologies. The three-dimensional flower bouquets built from the bunches of roses with surrounding fern fronds displayed the best adsorptivity and completely degraded methylene blue within 60 min under UV irradiation, whereas the humming-top geometry composed of anisotropically elongated spindle-like crystallites was detrimental to the dye photodegradation. (C) 2010 Elsevier Inc. All rights reserved.