Multi-walled carbon nanotube (MWCNT)/polypropylene (PP) composites were prepared by a micro melt mixing process. As-prepared composites had relatively low electrical conductivity due to the disruption of MWCNT network by strong shear. The electrical conductivity jumped to high values throughout an annealing process above the melting temperature of PP. The significant enhancement of electrical conductivity was influenced by annealing time, temperature, and content of MWCNTs. In particular, molecular weight of PP played an important role in affecting the conductivity enhancement. The molecular weight of PP was varied from 190,000 to 340,000 to examine its effect on the electrical conductivity. By comparing the conductivity enhancement behavior of composites with different molecular weight PPs and observing the morphology evolution during annealing, it was found that reaggregation of MWCNTs and the subsequent formation of MWCNT network during annealing are the main reasons for the jump of electrical conductivity. (C) 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 2238-2247, 2010