In order to easily and simply improve the cyclability of the Sn film negative electrode, we selected Co as a matrix metal and tried to prepare the Co-Sn alloy film negative electrode by a pulse electrodeposition method. The surface morphology of the deposit was almost the same as that of the Sn film, although aggregation partially occurred. The content rate of Co and Sn in the deposit was almost the same as the composition percentage in the electrodeposition bath. X-ray diffraction measurement showed that the deposited film could be assigned to a metastable Co-Sn alloy, while the co-deposition of crystalline Sn was not observed. The galvanostatic charge-discharge tests indicated that the discharge capacity and the charge-discharge efficiency of the Co30.5Sn69.5 alloy film electrode at the 1st cycle were 529.2 mAh g(-1) and 87.9%, respectively. Furthermore, the film electrode showed a good cyclability and discharge capacity of 470.5-617.5 mAh g(-1) during 50 cyclings. Alloying Sn with inactive Co could effectively improve the cyclability of the Sn film electrode prepared by the pulse electrodeposition method. (C) 2010 Elsevier B.V. All rights reserved.