The structure and thermal stability of self-assembled monolayers (SAMs) of benzenethiolate (BT) on Cu(100) have been studied by means of thermal desorption spectroscopy (TDS), scanning tunneling microscopy (STM), low-energy electron diffraction (LEED), UV photoelectron spectroscopy (UPS), X-ray photoelectron spectroscopy (XPS), and near-edge X-ray adsorption fine structure spectroscopy (NEXAFS). Vapor deposition at room temperature yields a well-ordered, densely packed c(6 x 2) saturation structure. At room temperature, this film is, however, metastable and transforms via partial decomposition by cleavage of the S-C bond into a less densely packed layer that reveals a coexisting p(2x2) phase. Such a transition occurs on a time scale of several days and is accompanied by a reduction of the work function change with respect to the bare Cu(100) surface from Delta phi = -0.9 eV for a freshly prepared saturated layer to -0.5 eV for an aged film. TDS experiments exhibit the presence of two distinct desorption channels (dissociative and intact desorption) occurring at different temperatures that reflects a variation of the local Cu S interaction strength of BT at differently coordinated adsorption sites. Heating to above room temperature causes a rapid degradation and continuous thinning of BT films whereas above 500 K all thiolate species have desorbed or dissociated, leaving a sulfide overlayer behind that is accompanied by a substrate reconstruction. Interestingly, the upright orientation of BT adopted in the saturated monolayer remains almost identical upon heating and demonstrates the absence of downward tilting upon thermally induced thinning of the film.