The aim of this work was to understand the evolution of powder tabletability and flowability during wetting and nucleation stages of high-shear wet granulation (HSWG). Microcrystalline cellulose (MCC) was granulated with water using a high-shear process. Granule morphology, surface texture, size, porosity, specific surface area, tabletability, and flowability were characterized. MCC granulated with 5% water showed no change in tabletability but significantly improved flowability, corresponding to smoother surfaces and lower surface area. From 5% to 25% water, tabletability decreased by 1/4 but flowability remained unchanged. Granule shape and porosity remained unchanged while surfaces were smoothened, leading to decreased surface area. From 25% to 35% water, MCC granules became more round. There was another sharp decrease in tabletability but powder flowability remained unchanged. Forty-five percent of water led to more particle rounding and commencement of nucleation, which only slightly impacted tabletability and flowability. From 0% to 45% water, granule size decreased slightly and could not explain the significant changes in powder tabletability and flowability. Deteriorated tabletability was instead caused by surface smoothing, granule densification, and granule rounding. Enhanced powder flowability was caused mostly by surface smoothing with granule rounding as a minor contributor. (C) 2011 Elsevier B.V. All rights reserved.