We used X-ray microdiffraction (XRMD) to investigate the crystallinity and strain relaxation of Ge thin lines with widths of 100, 200, 500 and 1000 nm selectively grown on Si(0 0 1) substrates using a patterned SiO2 mask by chemical vapor deposition. The variations of the strain relaxation in the line and width directions were also investigated in Ge thin lines with a width of 100 nm. After growth, crystal domains with very small tilt angles were detected in Ge lines with all four line widths. The tilt angle range was larger in thinner Ge lines. After annealing at 700 degrees C, the formation of a single, large domain with a specific tilt angle was detected by XRMD for Ge thin lines with widths of 100 and 200 nm. These experimental results reflect the effects of SiO2 side walls around the Ge thin lines on crystallinity and strain relaxation of Ge. (C) 2011 Elsevier Ltd. All rights reserved.