Bimetallic SCN ligand based single crystals of manganese mercury thiocyanate (MMTC), cadmium mercury thiocyanate (CMTC) and zinc cadmium thiocyanate (ZCTC) are grown by slow solvent evaporation technique. The growth mechanism and surface features are investigated by optical microscopic techniques such as scanning electron microscopy (SEM) and atomic force microscopy (AFM). The laser induced surface damage measurements were carried out using a Q-switched Nd:YAG laser at 1064nm with laser beam of 1.0 Hz and pulse duration 25 ps. The laser damage threshold values of MMTC, CMTC and ZCTC are found to be 15.9, 22.9 and 19.7 GW/cm(2), respectively. The SEM analysis of MMTC reveals the formation of elongated dendrite growth pattern caused by the fluctuations of Mn and Hg metal ligands when thiocyanate (SCN) bridges them. The etching study indicates the occurrence of different types of etch pit patterns like terraced triangles, pillars, pyramids and rods. The AFM images confirm the formation of three major hillocks with cavities in MMTC. The measured roughness values for CMTC crystal are very much lower than that of MMTC. (C) 2010 Elsevier B.V. All rights reserved.