In order to smooth the rough surface and further improve the wear-resistance of coarse chemical vapor deposition diamond films, diamond/tetrahedral amorphous carbon composite films were synthesized by a two-step preparation technique including hot-filament chemical vapor deposition for polycrystalline diamond (PCD) and subsequent filtered cathodic vacuum arc growth for tetrahedral amorphous carbon (ta-C). The microstructure and tribological performance of the composite films were investigated by means of various characterization techniques. The results indicated that the composite films consisted of a thick well-grained diamond base layer with a thickness up to 150 mu m and a thin covering ta-C layer with a thickness of about 0.3 mu m, and sp(3)-C fraction up to 73.93%. Deposition of a smooth ta-C film on coarse polycrystalline diamond films was proved to be an effective tool to lower the surface roughness of the polycrystalline diamond film. The wear-resistance of the diamond film was also enhanced by the self-lubricating effect of the covering ta-C film due to graphitic phase transformation. Under dry pin-on-disk wear test against Si3N4 ball, the friction coefficients of the composite films were much lower than that of the single PCD film. An extremely low friction coefficient (similar to 0.05) was achieved for the PCD/ta-C composite film. Moreover, the addition of Ti interlayer between the ta-C and the PCD layers can further reduce the surface roughness of the composite film. The main wear mechanism of the composite films was abrasive wear. (C) 2010 Elsevier B. V. All rights reserved.