CrN, TiCN and TiAlN coatings were deposited on WC cemented carbide disks using enhanced cathodic arc magnetron sputtering and their topographies and structures were observed and analyzed using scanning electron microscopy (SEM) and X-ray diffraction (XRD), respectively. The friction and wear properties of CrN, TiCN and TiAlN coatings sliding against SiC balls in water were investigated and compared synthetically using ball-on-disk tribometer. The results showed that the CrN/SiC tribopairs showed the lowest friction coefficient of 0.076, while the TiCN/SiC tribopairs displayed the highest friction coefficient of 0.264. For the CrN/SiC tribopairs the specific wear rate of CrN coatings was lowest while that of SiC balls became highest. But for the TiAlN(TiCN)/SiC tribopairs, the specific wear rate of TiAlN coatings was highest while that of SiC balls for the TiCN/SiC tribopairs became lowest. This indicated that the friction and wear behaviors of nitride coatings/SiC balls tribo-systems in water were more strongly influenced by the anti-oxidative ability of tribomaterials in water than by their mechanical properties. (C) 2011 Elsevier B. V. All rights reserved.