The influence of high-temperature annealing on the electrical properties and microstructure of tin-doped indium oxide (ITO) thin films was investigated as a function of oxygen gas flow ratio to argon gas during the sputtering deposition. The ITO thin films were annealed at 500 degrees C in air after the deposition. It was found that the ITO thin films, which were deposited in relatively low oxygen gas flow ratio, exhibited high Hall mobility and low-resistivity after the annealing. Furthermore, the X-ray reflectivity and diffraction measurement revealed that the ITO thin film with low-resistivity after annealing exhibited high packing density, smooth surface and low crystallization degree. It can be considered that the carrier electron scattering was suppressed with increasing in the packing density of the ITO thin film; as a result, the Hall mobility and resistivity were improved. (C) 2011 Elsevier B.V. All rights reserved.