Ni modified layer was prepared on surface of the Ti6Al4V substrate by plasma surface alloying technique. Surface morphology, micro-structure, composition distribution, phase structure, and microhardness of the Ni modified layer were analyzed. Tribological performance of the Ni modified layer and Ti6Al4V substrate was investigated by using pin-on-disc tribometer. The results indicate that roughness of the Ni modified layer was increased due to formation of the micro-convex on the modified surface. The concentration of Ni gradually decreased from the surface to interior. The maximum content of Ni atoms was nearly 90%. The modified layer was composed of TiNi, Ti2Ni and Ti phases. The maximum microhardness of the Ni modified layer was about 677 HV0.025 which was increased about two-fold of microhardness of the control Ti6Al4V substrate. Wear resistance of the Ni modified layer was improved obviously, and showed micro-abrasion wearing. The strengthened mechanism of the as-treated Ti6Al4V alloy is discussed. (C) 2011 Elsevier B.V. All rights reserved.