Chitosan is a polysaccharide derived from chitin, mainly of crustacean shells and shrimp wastes. The utilization of chitosan is related to the molar weight and deacetylation degree of the biopolymer. The aim of this work is to study the chitin deacetylation reaction, by the viscosity average molar weight and deacetylation degree of chitosan as a function of reaction time. Deacetylation was carried out in concentrated alkaline solution, 421 g L-1, at 130 degrees C and the reaction occurred during 4 h. Chitosan paste obtained after 20, 90 and 240 min was used to produce biofilms, which were characterized according water vapor permeability and mechanical properties (tensile strength and percentage tensile elongation at break). During the reaction time deacetylation degree reached 93%, and a 50% reduction in the viscosity average molar weight value in relation to the value of the first 20 min of reaction was found Both reactions presented a kinetic behavior of the pseudo-first order. Biofilm produced from the paste of chitosan with high deacetylation degree showed higher water vapor permeability (WVP), tensile strength (TS) and elongation (E) when compared to films with a low deacetylation. (C) 2011 Elsevier B.V. All rights reserved.