Korean Chemical Engineering Research, Vol.50, No.1, 1-5, February, 2012
Ba0.5Sr0.5Co0.8Fe0.2O3-δ 중공사 분리막의 제조 및 물성
Fabrication and Property of Ba0.5Sr0.5Co0.8Fe0.2O3-δ Hollow Fiber Membranes
E-mail:
초록
외경 1.02 mm, 내경 0.437 mm를 갖는 Ba0.5Sr0.5Co0.8Fe0.2O3-δ 중공사를 상전이 방적기술로 제조하였다. 초기 Ba0.5Sr0.5Co0.8Fe0.2O3-δ 선구 분말은 착체중합법을 이용하여 합성하였고, 900 ℃ 에서 하소하였다. 합성한 분말을 고분자 용액에 분산시킨 후 이중관형 노즐을 통해 중공사를 사출하였다. 최종적으로 산소분리에 사용 가능한 치밀 Ba0.5Sr0.5Co0.8Fe0.2O3-δ 중공사막을 1,080 ℃ 에서 2 시간 동안 소결하여 얻을 수 있었다. 또한 0.58 mm의 매우 얇은 분리막임에도 불구하고, BSCF 중공사 분리막은 602.5 MPa의 적당한 기계적 강도를 유지하였다.
Ba0.5Sr0.5Co0.8Fe0.2O3-δ hollow fiber with o.d. 1.02 mm and i.d. 0.437 mm were fabricated by a phaseinversion spinning technique.The starting Ba0.5Sr0.5Co0.8Fe0.2O3-δ precursor was synthesized by the polymerized complex method and then calcined at 900 ℃. As-prepared powder was dispersed in a polymer solution, and extruded as form of hollow fiber through a spinneret. Finallydense Ba0.5Sr0.5Co0.8Fe0.2O3-δ hollow fiber membrane was obtained by
sintering for 2 h at 1,080 ℃ for the application of oxygen separation. In addition, despite a very thin membrane with 0.58 mm, the BSCF hollow fiber membrane possessed a proper mechanical strength of 602.5 MPa.
- Luyten J, Buekenhoudt A, Adriansens W, Cooymans J, Weyten H, Servaes F, Leysen R, Solid State Ion., 135(1-4), 637 (2000)
- Bredesen R, Jordal K, Bolland O, Chem. Eng.Process., 43, 1129 (2004)
- Kvamsdal HM, Jordal K, Bolland O, Energy, 32(1), 10 (2007)
- Stiegel GJ, Maxwell RC, Fuel Process. Technol., 71(1-3), 79 (2001)
- Sunarso J, Baumann S, Serra JM, Meulenberg WA, Liu S, Lin YS, da Costa JCD, J. Membr. Sci., 320(1-2), 13 (2008)
- Dyer PN, Richards RE, Russek SL, Taylor DM, Solid State Ion., 134(1-2), 21 (2000)
- Bouwmeester HJM, Catal. Today, 82(1-4), 141 (2003)
- Leo A, Smart S, Liu S, Costa JCDD, J. Membr. Sci., 368, 64 (2011)
- Kim DH, Kim GL, Jo HD, Park JS, Lee HK, Korean Chem. Eng. Res., 48(5), 660 (2010)
- Kim DH, An YM, Jo HD, Park JS, Lee HK, Membr.J., 19, 244 (2009)
- Park HH, Deshwal BR, Jo HD, Choi WK, Kim IW, Lee HK, Desalination, 243(1-3), 52 (2009)
- Park HH, Deshwal BR, Kim IW, Lee HK, J. Membr. Sci., 319(1-2), 29 (2008)
- An YM, Kim DH, Jo HD, Seo YS, Park YS, Lee HK, Membr. J., 19, 261 (2009)
- Liu SM, Gavalas GR, Ind. Eng. Chem. Res., 44(20), 7633 (2005)
- Liu S, Tan X, Shao Z, da Costa JCD, AIChE J., 52(10), 3452 (2006)
- Wang H, Schiestel T, Tablet C, Schroeder M, Caro J, Solid State Ion., 177(26-32), 2255 (2006)
- Zydorczak B, Wu ZT, Li K, Chem. Eng. Sci., 64(21), 4383 (2009)