In this work, the corrosion behaviour of magnesium alloys ZK31, EZ33 and WE54 was studied in sodium borate buffer solution at pH 9.2. The electrochemical processes were studied by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). The composition and morphology of the alloys and corrosion products formed were studied by scanning electron microscopy (SEM), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The experimental findings highlighted the differences in the corrosion mechanisms of the different alloys tested. The results showed that the presence of rare-earth elements (RE) only increases the corrosion resistance when present in solid solution, as is the case of the WE54 alloy. At pH 9.2, an amorphous yttrium oxide/hydroxide thick film was formed, which possesses greater stability when compared to magnesium oxide/hydroxide. The role of RE in the corrosion mechanism was discussed. (C) 2010 Elsevier Ltd. All rights reserved.