Li3xLa2/3-xTiO3 (LLTO) powder with different lithium contents (nominal 3x=0.03-0.75) was synthesized via a simple sol-gel route and then calcination of gel-derived precursor at 900 degrees C which was much below the calcination temperature required for synthesizing the LLTO powder via solid state reaction route. The LLTO powder of sub-micron sized particles, derived from such sol-gel method, showed almost no aggregation. Starting from the sol-gel-derived powder, the LLTO ceramics with different lithium contents were prepared at different sintering temperatures of 1250 and 1350 degrees C. It demonstrated that our sol-gel route is quite simple and convenient compared to the previous sol-gel method and requires lower temperature for the LLTO. Our results also illustrated that lithium content significantly affects the structure and ionic conductivity of the LLTO ceramics. The dependence of the ionic conductivity on the lithium content, lattice structure, microstructure and sintering temperature was investigated systematically. (C) 2010 Elsevier Ltd. All rights reserved.