The nanocrystalline mordenite (MOR) type zeolite materials with initial chemical composition Na(2)O:Al(2)O(3):10SiO(2):48H(2)O have been synthesized under hydrothermal conditions. MOR1 and MOR2 are spherically shaped nanocrystals, whereas MOR3 and MOR4 have rod-like morphology. This paper reports the sorption characteristics of MOR analogues for Th(IV) and Eu(III) removal from aqueous nuclear waste. Sorption of Th(IV) and Eu(III) on MOR1, MOR2, MOR3 and MOR4 in a single component system with varying initial metal ion concentration, solution pH, contact times, sorbent dose and temperatures has also been investigated. Further, the Langmuir and Freundlich sorption models have been applied to describe equilibrium isotherms at different temperatures. The adsorption capacity increases largely with increasing solution pH and temperature of the system. Specific surface area and pore volume have been investigated by Brunauer-Emmett-Teller (BET) method. The N(2) adsorption isotherm presents a type IV isotherm with narrow hysteresis loop which indicates the presence of mesopores related to inter-particle voids. Thermodynamic results indicate that the sorption follows an endothermic physisorption process. It has been found that these exchangers have good sorption capacity and out of which MOR4 has highest sorption capacity. Thus, nanocrystalline MOR4 is proved to be good sorbent for both Th(IV) and Eu(III). (C) 2011 Elsevier Inc. All rights reserved.