Dense film mixed matrix membranes (MMMs) comprised of SSZ-13 dispersed in a crosslinkable polyimide (PDMC) were fabricated and evaluated for carbon dioxide/methane separations. MMMs containing 25% (w/w) as-received (AR) SSZ-13 exhibited a carbon dioxide permeability of 153 Barrers with a carbon dioxide/methane ideal selectivity of 34.7 at 65 psia and 35 degrees C. This represents a permeability enhancement of 129% and a decline in selectivity of 4.7% over neat PDMC (P(CO2) = 66.9 Barrers, alpha(CO2/CH4) = 36.4). A sieve surface modification procedure was developed with the aim of improving SSZ-13/PDMC MMM transport properties. MMMs containing 25% (w/w) surface modified (SM) SSZ-13 exhibited a carbon dioxide permeability of 148 Barrers and carbon dioxide/methane selectivity of 38.9 at 65 psia and 35 degrees C, representing enhancements in both permeability and selectivity of 121% and 6.9%, respectively. Mixed gas permeation analyses of MMMs containing SM-SSZ-13 using a 10% carbon dioxide/90% methane mixture shows that permeability and selectivity enhancements of 47% and 13%, respectively, over neat PDMC are possible at 700 psia and 35 degrees C. (C) 2011 Elsevier B.V. All rights reserved.