Periodic mesoporous organosilica (PMO) with polyhedral oligomeric silsesquioxane (POSS) air pockets integrated into the pore walls has been prepared by a template-directed, evaporation-induced self-assembly spin-coating procedure to create a hybrid POSS-PMO thin film. A 10-fold increase in the porosity of the POSS-PMO film compared to a reference POSS film is achieved by incorporating similar to 1.5 nm pores. The increased porosity results in a decrease in the dielectric constant, k, which goes from 2.03 in a reference POSS film to 1.73 in the POSS-PMO film.