In the present manuscript, we have demonstrated that hierarchically structured smart porous polymer films based on honeycomb-patterned surface can be elaborated from PS-b-P4VP pH-responsive block copolymer using the breath figure process. Despite the fast film formation by a bottom-up process, the copolymer nanostructuration was observed inside the walls of the honeycomb porous film. Atomic force microscopy (AFM), small angle X-ray and neutron scattering (SAXS and SANS) measurements were used to reveal both the hexagonal arrays formed by the pores at the micrometer length scale and the hexagonal copolymer self-assembly at the nanometer length scale. Contact angle (CA) measurements were used to point out the reversible pH-responsive wettability character of the surface. The PS-b-P4VP honeycomb film shows a contact angle variation of 20 degrees between pH 9 and pH 3. An increase of the roughness was obtained with the pincushions hexagonal array enhancing the pH responsiveness of the polymer film with a switching CA gap of 75 degrees when pH tuned from pH 9 to pH 3. This work presents the first report on honeycomb porous and pincushion films exhibiting a reversible pH-responsive character.