In this study, the effect of microstructure at the base metal (BM), the fine grain heat affected zone (FGHAZ), the coarse grain HAZ (CGHAZ) and weld metal (WM) under different welding heat input on hydrogen permeation in X80 steel weldments have been investigated. Base metal showed the highest effective diffusivity. With each heat input, the effective hydrogen diffusivity in FGHAZ is comparable to that of the base metal. The effective hydrogen diffusivity in weld metal was lower than that in CGHAZ. With increasing the welding heat input, the effective diffusivity in different zones of the weldment decreased correspondingly. Non-metallic inclusions were not detected in each specimen. Constituents in microstructure under low heat input are likely to agglomerate during accelerated cooling. The retained hydrogen may create an unpredictable susceptibility to hydrogen cracking at the CGHAZ even existing during service. (C) 2011 Elsevier B.V. All rights reserved.