0.92K(0.5)Na(0.5)NbO(3)-(0.08-x)Bi0.5Li0.5TiO3-xBaZrO(3) (KNN-BLT-BZ) lead-free piezoelectric ceramics were fabricated by traditional ceramics process. XRD results showed that complete solid solutions with mixed phases of rhombohedra and tetragonal were observed. Diffusion phase transitional behavior, dielectric properties and ferroelectric properties of the KNN-BLT-BZ ceramics were investigated. It was found that the cubic-tetragonal phase transition temperature (T-C) slightly decreased as the amount of BaZrO3 was increased. A morphotropic phase boundary (MPB) between rhombohedral and tetragonal ferroelectric phases was identified in the composition range of 0.04 <= x <= 0.06. Furthermore, good ferroelectric properties were also found in this composition range, with P-r of 14.5 mu C cm(-2) and E-c of 1.95 kV mm(-1) for the sample with x = 0.04. (C) 2011 Elsevier B.V. All rights reserved.