Emulsion polymerizations of several vinyl monomers, styrene, methyl methacrylate, butyl methacrylate, butyl acrylate, and vinyl acetate, in water using alkali-hydrolysable cationic surfactants with a betaine ester group (1-alkoxycarbonylmethyl)trimethylammonium chlorides, as emulsifiers were carried out and properties of the resulting latices and the polymers recovered by hydrolysis and salting out were investigated. There were little influences of the surfactants and monomers used here on the polymerizations, forming stable and monodisperse latices with a mean diameter of ca. 70 nm and giving a high molecular weight of polymers at high yields. All polymers were precipitated and recovered by adding a small amount of sodium hydroxide into the latex solutions contained little amount of ionic species. Solvent-cast films of the polymers were found to have surfaces as hydrophobic as those for the corresponding pure polymers prepared by bulk polymerization.