Nickel plating graphite nanosheets (Ni/GNs) were prepared by electroless plating method using graphite nanosheets (GNs). Then a novel polymer magnetic composites based on acrylate pressure-sensitive adhesive (acrylate PSA) filled with Ni/GNs were fabricated by solution blend method. The Ni/GNs and acrylate PSA/Ni/GNs composites were characterized by scanning electron microscope (SEM)/energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), vibrating sample magnetometer (VSM) and transmission electron microscope (TEM). All results showed that relatively uniform and compact Ni layer is successfully coated onto GNs under the given conditions, furthermore, Ni/GNs are homogeneously dispersed in acrylate PSA. The VSM results showed that the saturation magnetization of acrylate PSA/Ni/GNs composites increases with an increasing content of Ni/GNs while the coercivity decreases with an increasing content of Ni/GNs. When the content of GNs is 20 wt%, acrylate PSA/Ni/GNs composites exhibites good mechanical properties. (C) 2011 Elsevier B.V. All rights reserved.