Mesoporous Si-MCM-41 molecular sieve was synthesized hydrothermally and different wt.% of Sb (1.0, 2.0, 3.0, 5.0, 10.0, 15.0 and 20.0) was loaded on it by wet impregnation method. The Sb/MCM-41 materials were characterized by various physico-chemical techniques such as XRD, TGA and TEM. The TEM image showed a honeycomb structure of the host material. They were used as catalytic templates for the growth of MWCNTs by CVD method with different temperatures at 700, 800, 900 and 1000 degrees C using acetylene as a carbon precursor. The reaction temperature was optimized for the better formation of MWCNTs and they were purified and then characterized by XRD, SEM, HR-TEM and Raman spectroscopy techniques. The formation of MWCNTs with diameter in the range of 4-6 nm was observed from HR-TEM. The good thermal stability and high productivity of catalyst observed in this study revealed that the 2 wt.% Sb loaded MCM-41 could be a promising support for the catalytic synthesis of MWCNTs at 800 degrees C by CVD method. (C) 2011 Elsevier B.V. All rights reserved.