InN films with the wurtzite structure have been grown directly on YSZ (1 0 0) substrate by the RF-magnetron sputtering technique. Strongly (0 0 2) oriented films with smooth surfaces (0.7-2.9 nm surface roughness depending on substrate temperature), were grown within 30 min. Films deposited for 60 min developed three-dimensional (3D) pyramidal islands on top of their surfaces, which diminished the residual elastic strain. The optical absorption edge and PL peak energy around 1.7 eV were found to redshift with increasing film thickness and substrate temperature. (C) 2012 Elsevier B.V. All rights reserved.