Hydrothermal carbonization of cellulose, lignin, D-xylose (substitute for hemicellulose), and wood meal (WM) was experimentally conducted between 225 and 265 degrees C, and the chemical and structural properties of the hydrochars were investigated. The hydrochar yield is between 45 and 60%, and the yield trend of the feedstock is lignin > WM > cellulose > D-xylose. The hydrochars seem stable below 300 degrees C, and aromatic structure is formed in all of these hydrochars. The C content, C recovery, energy recovery, ratio of C/O, and ratio of C/H in all of these hydrochars are among 63-75%, 80-87%, 78-89%, 2.3-4.1, and 12-15, respectively. The higher heating value (HHV) of the hydrochars is among 24-30 MJ/kg, with an increase of 45-91% compared with the corresponding feedstock. The carbonization mechanism is proposed, and furfural is found to be an important intermediate product during D-xylose hydrochar production, while lignin hydrothermal carbonization products are made of polyaromatic hydrochar and phenolic hydrochar. The formation of microspheres on the surface of cellulose and WM hydrochars is discussed, and transformation of the hemicellulose should be the reaction for WM microsphere production.