| 초록 |
We propose to use the carbon nanofiber as a conductive substrate for the anode of RZMBs, which was prepared via heat treatment of electrospun PAN-derived nanofiber. Through CV and SEM results performed at a constant current rate of 20 mA cm-2, the optimum amount of zinc deposited on the CNF was determined to be 10 mAh cm-2. Symmetric cell test for 400 hours showed 60.1% reduction in plating/stripping overpotential when zinc deposited carbon nanofiber was used. This overpotential reduction was attributed to the macroporous structure of ZnCNF and the preferred orientation of zinc to the (002) plane as confirmed by post mortem analyses. RZMB full cells pairing ZnCNF with β-MnO2 were configured to deliver the 5C-rate capacity of 106.54 mAh g-1, which was higher 34.13 mAh g-1 with bare zinc. Finally, the long-term cyclability of ZnCNF || MnO2 with much lower N/P ratio of 18.0 was confirmed, demonstrating the capacity retention of 89.4%, greater than 73% of bare zinc || MnO2 cell with the N/P ratio of 234.6 over 300 cycles. |