제목 Performance degradation study of direct methanol fuel cell consists of PtRu and Pt black catalysts
초록 Direct methanol fuel cell (DMFC) is widely studied as a portable power source with longer life time than lithium-ion batteries. Among the obstacles to be overcome for commericialization of DMFC, stability of catalysts is one of most important point, which determines the life time of DMFC. In the present study, performance degradation of membrane electrode assembly (MEA) with PtRu and Pt catalysts was shown with the change of catalysts. The MEAs were prepared by the decal transfer method. Catalyst loading was 2 mg/cm2 for both the PtRu (anode) and Pt (cathode) catalysts. The prepared MEAs were operated at a constant current of 100 mA/cm2. Operation conditions were 1 ml/min 1 M methanol for anode and 100 cc/min oxygen at 55 oC. Maximum power density decreased from 62.9 mW/cm2 to 55.6, 49.2, 40.6, 35.2, 26.6 and 26.3 mW/cm2 with operation time from 0 to 120, 240, 432, 720, 912 and 1176 hours. In XRD study, peak shift was observed in the PtRu catalyst, while no change was shown in the Pt catalyst. Particle size was calculated from the XRD results and agglomeration of the PtRu catalyst was observed, while no change was shown in the Pt catalyst.
저자 전민구1, 오광석2, Li Shuang1, 이기락2, 원정연1, 홍대식2, 우성일1
소속 1한국과학기술원 생명화학공학과, 2초미세화학공정시스템연구센터
키워드 direct methanol fuel cell; catalyst; sintering
E-Mail siwoo@kaist.ac.kr
VOD VOD 보기
원문파일 초록 보기