| 제목 |
Fabrication of Bulk Hetero-Junction Solar Cells by Using P3HT/PCBM Blend |
| 초록 |
Fabrication of bulk hetero-junction solar cells was investigated by using blend of [6,6]-phenyl-C61-butyric acid methyl ester (PCBM) and poly (3-hexylthiophene) (P3HT). The ITO (7.9Ω/sq) coated glass substrate was cleaned in TCE, acetone, methanol for 30 min. Thin layer of poly (3,4-ethylene dioxy thiophene) doped with poly (styrene-sulfonate) acid (PEDOT:PSS) was spin-coated at 5000 rpm for 30s on a cleaned ITO-coated glass substrate and dried at 100 oC for 30 min. Photoactive layer (PCBM/P3HT) solution was spin-coated at 4000 rpm for 30s to form 150 (± 5)-. nm-thick film. Finally, 100 nm-thick Al metal electrodes were evaporated on top of the active layer. It thickness was measured using surface profiler (alpha step) and the current-density-voltage (I-V) characteristics of the cells were measured both in the dark and under illumination at 80 mW/cm2 by using an A.M 1.5 G solar simulator in the air. Power conversion efficiency was obtained reach to 1%. To improve power conversion efficiency, the studying of active layer morphology and thermal annealing effect was considered so far. |
| 저자 |
TRUONG NGUYEN NHU QUYNH, 이은국, 정재학
|
| 소속 |
영남대 |
| 키워드 |
solar cell; bulk hetero-junction; PCBM
|
| E-Mail |
|
| 원문파일 |
초록 보기 |