| 초록 |
Tungsten oxide (WO3) nanorods were applied for the first time as photoelectrodes in dye-sensitized solar cells (DSSCs). The DSSC based on WO3 nanorods showed a short-circuit current, an open-circuit voltage, a fill factor, and a conversion efficiency of 4.66 mA/cm2, 0.383 V, 0.22, and 0.75 %, respectively. The WO3 nanorod photoelectrode was treated with TiCl4 aqueous solution to improve the dye absorption and open-circuit voltage by coating the thin TiO2 layer on the WO3 nanorod surface. As a result, it was confirmed that the anatase TiO2 nanoparticles with size of 8 nm was coated on the WO3 nanorod surface. The TiCl4 treatment resulted in the enhanced performance of the short-circuit current of 6.75 mA/cm2, the open-circuit voltage of 0.457 V, the fill factor of 0.489, and the conversion efficiency of 1.51 %. These values can be compared with 5.55 mA/cm2, 0.447 V, 0.423, and 1.05 % for the photoelectrode based on the TiCl4-treated WO3 nanoparticles. The higher short-circuit current and fill factor for the nanorods compared with the nanoparticles can be attributed to the high charge transport property of the 1-D nanostructure. |