To form Al-Ta alloys for high temperature oxidation resistance components, molten salt electrolysis was carried out in an AlCl3-NaCl-KClmelt containing TaCl5 at 423 K. The voltammogram showed two cathodic waves at 0.45 V and 0.7 V vs. Al/Al(III), which may correspond to reduction from Ta(V) to Ta(III) and from Ta(III) to tantalum metal, respectively. Electrodeposits of Al and Ta were obtained in the range from 0.05 to 0.3 V and the highest concentration of Ta in the electrodeposit was 72 at% at 0.3 V. With increasing Ta content in the alloy, the morphology of the electrodeposits became powdery and the particle size smaller. (C) 2016 Elsevier B.V. All rights reserved.