A series of polyamic acids were prepared in N,N-dimethylactamide (DMAc) containing large amount of water, some of which contain the amount of water up to 25%. Their inherent viscosities decreased with the increase of water in DMAc, depending on the electronic properties of dianhydride and reaction condition. The molecular weights and mechanical properties of the polyimides thermally imidized from the polyamic acids were almost independent on the water content in solvent. The decomposition-resynthesis of polyamic acids during the curing was also investigated.