Poly(phenylacetylene)s bearing dialkylamino groups were prepared by the polymerization of p-(N,N-dialkylamino)phenylacetylenes with [Rh(nbd)Cl](2), and their electrochemical behavior was examined. Rh-catalyzed polymerization of p-(N,N-diethylamino)phenylacetylene (DEAPA) and p-(N,N-di-n-butylamino)phenylacetylene (DBAPA) in toluene in the presence of triethylamine gave good yields of the polymers (86 and 90%, respectively). Poly(DEAPA) was soluble in chloroform and dichloromethane, and poly(DBAPA) dissolved in various solvents such as toluene, THF, dichloromethane and chloroform. Poly(DEAPA) and poly(DBAPA) showed onset temperatures at 248 and 190 degrees C; respectively, and absorptions around 300-400 nm. Electrochemical doping of the polymer films resulted in the shift of the absorptions to a region around 680 nm, which accompanied a color change of the polymer films from green ocher to deep blue.